High Mechanical Strength Low Porosity Fire Clay Brick For Hot Metal Mixer Ladle, Coke Dry Quenching Laurel-01-03 manufacturer from China Qingdao Laurel Enterprise CO.,Ltd

High Mechanical Strength Low Porosity Fire Clay Brick For Hot Metal Mixer Ladle, Coke Dry Quenching

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: Laurel-01-03

High Mechanical Strength Low Porosity Fire Clay Brick For Hot Metal Mixer Ladle, Coke Dry Quenching Device
<

High Mechanical Strength Low Porosity Fire Clay Brick For Hot Metal Mixer Ladle, Coke Dry Quenching Device

Dense and Low Porosity Fire Clay Brick

Specifications:

Technical data

Item	High duty	Super duty
AL2O3%	38-42	42-45
Fe2O3%	1.8	1.7
SiO2%	56%	53%
Refractoriness	1730	1750
Apparent Porosity%	17Max	17Max
Refractoriness under load at 0.2MPa	1420	1450
cold crushing strength ≥	40Min	45Min
Linear Change on reheating 1450C*3H	-2+0	-0.1+0.05
BD g/cm3≥	2.2-2.4	2.3-2.4

Description:

The low Porosity clay refractory bricks are made of super calcined flint clay and calcined bauxite, With high Pressure formed and high temperature sintered. Due to its low apparent porosity, Strong resistance to erosion and high refractoriness under load, They are wildly used in Glass kiln, Blast furnace, Metal mixer Furnace, Hot metal mixer ladle, Coke dry quenching devices , etc.

Features:

1. Low porosity,High bulk density.

2. Good Cold Crushing strength.

3. High refractoriness under load.

4. High mechanical strength.

5. Good resistance to erosion.

Applications:

1. Glass kiln

2. Blast furnace

3. Metal mixer Furnace,

4. Hot metal mixer ladle

5. Blast furnaces