High Strength Industrial Silica Refractory Brick For Hot Blast Furnace, Coke oven 

Place of Origin: Zhejiang, China (Mainland) 
inquire
Add to My Favorites
HiSupplier Escrow
Share |

Product Detail

Model No.: Laurel-04-1


High Strength Industrial Silica Refractory Brick For Hot Blast Furnace, Coke oven
 
<span style="f

High Strength Industrial Silica Refractory Brick For Hot Blast Furnace, Coke oven

 

Description:
Our factory product various kinds of refractory products. The products can be made according with the customers' requirement.

Laurel can produces a large range of silica brick for many kind of industry usage.

SiO2 content: Above 95%.
Al2O3 content: Below 1.0%.
Usage: Hot-blast stove.

 

Features:

  1. Silicon oxide is above 95%.
  2. Good acid erosion resistance.
  3. High softening point with temperature.
  4. No shrink in burn repeatedly.
  5. Temperature of refractoriness under load is above 1650º C

 

Applications:

  1. Glass furnace
  2. Coke oven
  3. Blast furnace

 

Specifications:

Technical data

Silica brick for glass furnace

Item:

GF-96A

GF-96B

GF-95A

GF-95B

SiO 2

≥96

≥96

≥95

≥95

Fe 2 O 3

≤0.8

≤1.0

≤1.2

≤1.2

Apparent porosity %

≤22(24)

Cold Crushing

Strength MPa

Brick below20KG

≥35(30)

Brick ≥20KG

≥30(25)

Refractoriness under load ºC

≥1680

≥1670

≥1660

≥1650

True density g/cm ³

≤2.34

≤2.34

≤2.35

≤2.35

Silica brick for coke oven

Item:

CO-94A

CO-94B

SiO2: %

≥94

≥94

bigPhoto
 Ms. Jacky Liu
Sales Manager
Tel: 86-532-80829560
Fax: 86-532-80829650
Contact to this supplier

Related Search

Find more related products in following catalogs on Hisupplier.com

Company Info

Qingdao Laurel Enterprise CO.,Ltd [China (Mainland)]


Business Type:Manufacturer, Trading Company, Other
City: Qingdao
Province/State: Shandong
Country/Region: China (Mainland)

You May Like: